Process for the preparation of improved dyestuff granules from suspension containing a propylene oxide-ethylene oxide copolymer

ABSTRACT

To prepare storage-stable, low-dusting dyestuff granules which are readily soluble in plastics, a suspension of the dyestuff containing 0.1-5% by weight of a polyglycol are dried while being granulated.

The invention relates to a process for the preparation of dyestuffpreparations in granule form.

Processes in which dyestuffs for plastics are dried in a vacuum cabinetor paddle drier are known. In these processes, the dyestuff particleshave to be ground in a mill addionally. A very large amount of dustforms during this operation, and this of course results in losses. Highsuction must be applied to avoid a dust nuisance to the operatingpersonnel.

Processes for the preparation of dyestuff preparations in granule orpowder form in which dispersions or preferably solutions of dyestuffsand if appropriate plasticizers, surfactants and other auxiliaries aresprayed into melts of waxes and/or resins which are insoluble orsparingly soluble in water.

Disadvantages of the known processes are the dust nuisance and the highconcentrations of surfactants, dispersing auxiliaries and otheradditives employed to avoid this nuisance.

The invention was based on the object of providing an improved processfor the preparation of free-flowing, low-dusting granules with a smalladdition of auxiliaries, if possible of below 5%.

The invention relates to a process for the preparation of storage-stableand low-dusting dyestuff granules which are readily soluble in plastics,characterised in that a suspension of the dyestuff containing 0.1-5% byweight, based on the dry dyestuff, of a polyglycol is dried while beinggranulated.

In a preferred embodiment, the polyglycol has a molecular weight of900-15,000, in particular 5,000-8,000, calculated from the OH number. Inanother preferred embodiment, the polyglycol is a copolymer of propyleneoxide and ethylene oxide. In another preferred embodiment the polyglycolis a copolymer of propylene oxide and ethylene oxide having an averagemolar mass, calculated from the OH number, of between 2,000 and 10,000.In another preferred embodiment, the weight of the polyglycol is 1-3%,based on the dry dyestuff. In another preferred embodiment, the mixturecontains, in addition to the polyglycol, polyacrylic acid and/or saltsthereof, in particular sodium salts, in particular up to 2%, based onthe dry content of the dyestuff. In another preferred embodiment, arotating disc or pressure jet is used as the atomising element duringthe granulation.

In a preferred embodiment, the dyestuff suspension is an aqueoussuspension. In another preferred embodiment, the granulation takes placeby spray drying. A rotating disc or a pressure jet as described inChemiker Ztg./Chem. Apparatur/Verfahrenstechnik, Volume 93 (1969) No. 13is advantageously used as the atomising element. In another preferredembodiment, the free material is sifted by means of an annular channelor outside the drier, e.g. in a subsequent fluidised bed. The granulatedfree material can be regranulated after liquefaction. In anotherpreferred embodiment, the aqueous press-cake of the dyestuff is stirredin water. After stirring and homogenisation, it is then subjected to wetgrinding, for example in a rotor-stator mill and/or bead mill. Thedispersion thus formed with a particle size of between 1 and 50 μm isthen spray-dried to microgranules in an atomising drier, preferably apressure jet tower.

The intake and discharge temperatures here depend, alongside therequired residual moisture of ≦0.5%, on the safety measures.Microgranules of between 50 and 300 μm which, in contrast to the powder,are low-dusting and free-flowing are obtained by this process. Thegranules are storage-stable, that is to say the granules are notdestroyed by stresses, for example during transportation. In contrast,if spray-drying is carried out without the addition according to theinvention, the microgranules do not have the stability, theydisintegrate and are no longer low-dusting, and their ability to flow isgreatly reduced.

The choice of dyestuff essentially depends on the particular intendeduse of the preparations. All the customary water-insoluble dyestuffs ofthe most diverse chemical classes are in principle possible, includingwhiteners, for example

styrene

pyrazolone

quinophthalone

naphthazine

perinone

anthraquinone

coumarin

thioxanthal

thioindigo

monoazo

disazo

The proportion of dyestuff content in the granules is in general 95 to99% by weight.

The particle sizes of the microgranules can vary within wide ranges andare in general 5 to 800 μm, and preferably 50 to 300 μm.

The microgranules are in general advantageously prepared by a procedurein which the dyestuff press-cake is first intensively mixeddiscontinuously with the auxiliary in a stirred kettle and ifappropriate the mixture is heated, the temperature and solids contentbeing chosen so that the resulting dispersion of the dyestuff can easilybe atomised. By selecting a suitable atomising element, the atomisationcan be carried out so that the particle diameters of the resultingspherical granules are within the preferred ranges. The preferred rangeof 40 to 800 μm is obtained by spraying with one-component nozzles underpressures of up to 100 bar.

The formulations obtainable according to the invention are low-dustingand free-flowing.

The granules prepared by the new process have many possible uses: forexample, they are suitable for colouring plastics.

Particularly suitable plastics are ABS, polycarbonate, butylstyrenes,polyesters, polystyrenes and polyamides, as well as blends of theabovementioned plastics.

The colouring of the plastics with the dyestuff granules preparedaccording to the invention is preferably carried out in bulk, asdescribed, for example, in Coloring of Plastics, John Wiley and Sons,N.Y., 1979.Iadd., e.g. by dissolution in the molten or dissolvedplastic.Iaddend..

The quality of the granules can be increased by carrying out a siftingoperation, as described, for example, in U.S. application Ser. No.4,198,264. The fine material can be stirred up and spray-dried again.

Compared with drying in a paddle drier and grinding, the processdescribed has the advantage that significantly less dust nuisance occursduring preparation, since the operations from vigorous mixing to thespray-dried granules are carried out in an aqueous phase, andfurthermore dry grinding with the known losses is dispensed with, sothat the process described leads to a significantly higher yield.

EXAMPLE 1

2 parts of a copolymer of propylene oxide and ethylene oxide having anaverage molar mass--calculated from the OH number--of about 6,500 g/molare mixed with 322.5 parts of an aqueous press-cake or the dyestuff ofthe formula ##STR1## and 675.5 parts of water at room temperature, withvigorous stirring. The press-cake has a solids content of 61.4%. After astirring time of about 30 minutes, this approximately 20% strengthdispersion solid content is ground in one pass in a bead mill containingbeads of 2 mm in size. The dispersion then has an average particlediameter of about 30 μm. This dispersion is then spray-dried tomicrogranules in a pressure jet tower at an intake temperature of 180°C. and a discharge temperature of 85° C., with constant stirring of thefeed mixture. The resulting microgranules have an average particlediameter of about 250 μm and their residual moisture content is 0.3%.The granules are free-flowing and low-dusting.

EXAMPLE 2

1.8 parts of a copolymer of propylene oxide and ethylene oxide having anaverage molar mass of about 6,500 g/mol are mixed with 4.8 parts of apolyacrylic acid having an average molar mass of about 3,000 g/mol,461.8 parts of an aqueous press-cake of the dyestuff of the formula##STR2## and 531.9 parts of water at room temperature, while stirringvigorously. The press-cake has a solids content of about 63.6%. After astirring time of about 30 minutes, this approximately 30% strengthsuspension is ground in one pass in a bead mill containing beads of 2 mmin size. The pH of the dispersion is brought to the pH of about 6 withNaOH. The dispersion then has an average particle diameter of about 25μm. This dispersion is then spray-dried to microgranules in a pressurejet tower at an intake temperature of 205° C. and a dischargetemperature of 88° C., with constant stirring of the feed mixture. Theresulting microgranules are free-flowing and low-dusting, the averageparticle size is about 180 μm and the residual moisture content is about0.1%.

EXAMPLE 3

The following dyestuffs are also finished and spray-dried tomicrogranules in accordance with Examples 1 and 2: ##STR3##

We claim:
 1. Process for the preparation of storage-stable, low-dustingdyestuffs granules that are readily soluble in plastics, said process.Iadd.being .Iaddend.characterized in that a suspension of (a) awater-insoluble or sparingly-soluble-in-water dyestuff, (b) 0.1 to 5% byweight, based on the dry dyestuff, of a polyglycol which is a copolymerof propylene oxide and ethylene oxide, and (c) .Iadd.optionally.Iaddend.up to 2%, based on the dry dyestuff, of polyacrylic acid and/orsalts thereof, is dried while being granulated .Iadd.with spraydrying.Iaddend., the polyglycol having a molecular weight of 900-15,000,calculated from the OH.Iadd., the granules comprising 95 to 99% byweight of the dyestuff.Iaddend..
 2. Process according to claim 1,characterised in that an aqueous suspension of the dyestuff is used. ..3. Process according to claim 1, characterised in that the granulationis carried out with spray drying..!. . Process according to claim 1,characterised in that the polyglycol is a copolymer of propylene oxideand ethylene oxide having an average molar mass, calculated from the OHnumber, of between 2,000 and 10,000. . .5. Process according to claim 1,characterised in that the weight of the polyglycol, based on the drydyestuff, is not more than 5%..!.6. Process according to claim 1,characterised in that a rotating disc or pressure jet is used as ..the.!. .Iadd.an .Iaddend.atomising element during granulation. 7.Process for colouring plastics by granules obtained according to claim1, characterised in that the granules are dissolved in the molten ordissolved plastic.
 8. Process according to claim . .5.!..Iadd.1.Iaddend., characterized in that the weight of the polyglycol,based on the dry dyestuff, is 1-3%. .Iadd.9. Process according to claim1, wherein the suspension contains the polyacrylic acid or saltsthereof..Iaddend.